Black 1 Core 2 Core 3 Core Heat Shrink Breakout Waterproof Insulating Breakouts
• Manufactured from cross-linked polyolefin
• Provide sealing protection and strain relief over multi-core cable crutch, including 2-, 3-, 4—, and 5-core breakout
• Coated with adhesive on the body and the fingers to form a watertight seal
• Flame-retardant breakouts are available upon customer request
• Meeting with varieties of configuration requirements
• Shrink temperature: start at 90°C, and fully recovered at 130°C.
Technical Data
| Property | Test Method | Standard Value | ||
| Insulated Breakout | Oil Resistant Breakout | Semi-conductive Breakout | ||
| Tensile Strength | ASTM-D-638 | Ml2MPa | ml2MPa | X2MPa |
| Elongation at Break (1200 ,168 hrs) | ASTM-D-638 | 3=300% | 3300% | ^300% |
| Tensile Strength after Aging (120口 ,168 hrs) | ASTM-D-638 | ^10MPa | NlOMPa | AOMPa |
| Elongation at Break after Aging | ASTM-D-638 | "230% | "230% | "230% |
| Tensile Strength after Dipping | ASTM-D-638 | — | ROMPa | — |
| Elongation at Break after Dipping | ASTM-D-638 | — | 3230% | — |
| Dielectric Strength | IEC 60243 | 5kV/mm | ml 5kV/mm | — |
| WaterAbsorption | ISO 62 | <0.5% | W0.5% | <0.5% |
| Volume Resistivity | IEC 60093 | R x 1013Q • cm | ml x 1013Q • cm | 102 -104 Q - cm |