1/8 3.2mm Black Dual Wall Adhesive Lined Cross-Linked Polyolefin Tubing
Adhesive lined heat shrink tubing ideal for applications where both exceptional flame retardancy and environmental sealing capabilities are required.
Features
• 3:1&4:1 shrink ratio
• Highly flame retardant
• Superior sealing against water, moisture or other contaminants
• High shrink ratio allows for coverage of irregularly shaped connectors and components
• Superior sealing against water, moisture and other contaminants
• Continuous operating temperature:-55°C-135°C
• Fully shrink temperature:^125°C
• Meets MIL-DTL-23053/4
Dimensions
SBRS-(3X)GF
| Size | Expanded | After Recovery | Standard Package | |||
| Inch | mm | Internal Diameter mm | Internal Diameter mm | Total Wall Thickness mm | Adhesive Thickness mm | Spool Lenath M/spooF |
| 1/8 | 3.2 | 3.2 | 1.0 | 0.90±0.30 | 0.40±0.20 | 200 |
| 3/16 | 4.8 | 4.8 | 1.6 | 1.05±0.30 | 0.40±0.20 | 100 |
| 1/4 | 5.4 | 5.4 | 2.2 | 1.25±0.30 | 0.45±0.20 | 100 |
| 5/16 | 7.9 | 7.9 | 2.7 | 1.35±0.30 | 0.45±0.20 | 100 |
| 3/8 | 9.5 | 9.5 | 3.2 | 1.45±0.30 | 0.50±0.20 | 50 |
| 1/2 | 12.7 | 12.7 | 4.2 | 1.650±0.30 | 0.50±0.20 | 1.22OR25M/Roll |
| 5/8 | 15 | 15 | 5.2 | 1.80±0.30 | 0.55±0.30 | 1.22OR25M/Roll |
| 3/4 | 19.1 | 19.1 | 6.3 | 1.95±0.30 | 0.60±0.30 | 1.22OR25M/R0II |
| 1 | 25.4 | 25.4 | 8.5 | 2.00±0.40 | 0.60±0.30 | 1.22OR25M/R0II |
| 1-1/4 | 30 | 30 | 10.2 | 2.15±0.40 | 0.65±0.30 | 1.22OR25M/Roll |
| 1-1/2 | 39 | 39 | 13.5 | 2.45±0.40 | 0.75±0.30 | 1.22OR25M/Roll |
| 2 | 50 | 50 | 17.0 | 2.75±0.40 | 0.80±0.30 | 1.22OR25M/Roll |
SBRS-(4X)GF
| Size | Expanded | After Recovery | Standard Package | |||
| Inch | mm | Internal Diameter mm | Internal Diameter mm | Total Wall Thickness mm | Adhesive Thickness mm | Spool Length M/spool |
| 5/32 | 4.0 | 4,0 | 1.0 | 1.05±0.30 | 0.50±0.20 | 200 |
| 1/4 | 6.0 | 6,0 | 1.5 | 1.15±0.30 | 0.50±0.20 | 100 |
| 5/16 | 8.0 | 8,0 | 2.0 | 1.55±0.30 | 0.60±0.25 | 50 |
| 1/2 | 12.0 | 12,0 | 3.0 | 1.75±0.30 | 0.60±0.25 | 1.22OR25M/R0II |
| 5/8 | 16.0 | 16,0 | 4.0 | 2.00±0.35 | 0.70±0.30 | 1.22OR25M/Roll |
| 25/32 | 20.0 | 20,0 | 5.0 | 2.30±0.40 | 0.70±0.30 | 1.22OR25M/Roll |
| 1 | 24.0 | 24,0 | 6.0 | 2.60±0.40 | 0.75±0.30 | 1.22OR25M/Roll |
| 1-1/4 | 32.0 | 32,0 | 8.0 | 3.00±0.50 | 0.90±0.30 | 1.22OR25M/Roll |
| 2 | 52.0 | 52,0 | 13.0 | 3.35±0.50 | 0.95±0.30 | 1.22OR25M/Roll
|
Technical Data
| Tensile Strength(MPa) | ASTM D2671 | m12 | 12.5 |
| Elongation(%) | ASTM D2671 | XOO | 450 |
| Tensile Strength after aging (MPa) | MIL-DTL-23053/4 | N8.4 | 8.5 |
| Elongation after aging(%) | MIL-DTL-23053/4 | ^100 | 350 |
| Dieletric strength(kv/mm) | IEC 60243 | M15 | 17.5 |
| Volume resistivity(Q.cm) | IEC 60093 | 3s1X1014 | 2.5X1014 |