Changzhou Longchuang Insulating Material Co., Ltd.
Manufacturer of good insulation materials； Your long-term partner !
Add to Cart
Black Heat Shrink Semi-Conductive Tube Shrink Temperature Start At 90°C And Fully Recovered At 130°C
・ Manufactured from cross linked semi-conductive polyolefin
・ Shrink temperature: start at 90°C, and fully recovered at 130°C
・ Color: black
Selection Table
| Product No. | Inner Diameter/mm | After Recovered Wall Thickness (±0.2)/mm | Standard Cut Length/mm | Standard Continuous Length (m/roll) | |
| As 腳 led | After Recovered (Max) | ||||
| WRSBG-45/17 | 45 | 17 | 2.3 | 400-1200 | 25 |
| WRSBG-50/17 | 50 | 17 | 2.3 | 400-1200 | 25 |
| WRSBG-50/19 | 50 | 19 | 2.3 | 400-1200 | 25 |
| WRSBG-55/19 | 55 | 19 | 2.3 | 400-1200 | 25 |
| WRSBG-55/23 | 55 | 23 | 2.3 | 400-1200 | 25 |
| WRSBG-60/23 | 60 | 23 | 2.3 | 400-1200 | 25 |
| WRSBG-60/25 | 60 | 25 | 2.3 | 400-1200 | 25 |
| WRSBG-65/25 | 65 | 25 | 2.3 | 400-1200 | 25 |
| WRSBG-75/29 | 75 | 29 | 2.8 | 400-1200 | 25 |
| WRSBG-80/29 | 80 | 29 | 2.8 | 400-1200 | 25 |
| WRSBG-85/29 | 85 | 29 | 2.8 | 400-1200 | 15 |
| WRSBG-100/29 | 100 | 29 | 2.8 | 400-1200 | 15 |
| WRSBG-100/35 | 100 | 35 | 2.8 | 400-1200 | 15 |
| WRSBG-120/35 | 120 | 35 | 2.8 | 400-1200 | 15 |
| Technical Data | |||||
| Property | Test Method | Standard Value | |||
| Tensile Strength | ASTM-D-638 | Ml3MPa | |||
| Elongation at Break | ASTM-D-638 | M300% | |||
| Tensile Strength after Aging | ASTM-D-638 | ^10.5MPa(130r,168hrs) | |||
| Elongation at Break after Aging | ASTM-D-638 | N240% (130r,168hrs) | |||
| Volume Resistivity | IEC 60093 | ml x 105Q • cm | |||
| Longitudinal Shrinkage | ASTM-D-2671 | W10% | |||
| Eccentricity | ASTM-D-2671 | <30% | |||
| WaterAbsorption | ISO 62 | W0.5% | |||